High impact, high elongation resin
A high-strength engineering plastic with good impact resistance and excellent surface finish. Ideal for a wide variety of tools in the production floor including tooling, manufacturing aids, and housings as well as for consumer goods.
*All specimen were conditioned in ambient lab conditions at19-23C / 40-60% RH for at least 24 hours. See more details in Technical Data Sheet.
| Testing Method | Green | Post-Processed | |
| Tensile Stress at Break |
ASTM D638 | 24 ± 1 MPa | 45 ± 2 MPa |
| Tensile Modulus | ASTM D638 | 897 ± 20 MPa | 1434± 80 MPa |
| Elongation at Break |
ASTM D638 | 89 ± 9% | 101 ± 11% |
| Flexural Modulus | ASTM D790 | 826 ± 27 MPa | 1383 ± 63 MPa |
| IZOD Impact (Notched) | ASTM D256 | N/A | 51 ± 4 J/m |
| Heat Deflection Temp.@0.455 MPa | ASTM D648 | N/A | 52.8°C |